为了研究四川藏区传统牦牛酸奶中高产胞外多糖乳酸菌特性及发酵性能，以本实验室分离出的六株高产胞外多糖乳酸菌为研究对象，以菌株生长量、耐酸性、胆盐耐受力、渗透压耐受力和细胞表面疏水性为指标进行特性研究；以发酵酸奶的凝乳时间、持水力、酸化及后酸化能力、挥发性物质及质构等为指标进行发酵性能研究。菌株的生长曲线表明，6株菌株分别在14 h（218、276、266）、16 h（271、285、231）进入对数生长稳定期，其中编号218的菌株生长量最高，OD值为2.188。耐受性实验结果表明，菌株276具有良好的耐酸能力（P<0.05）；菌株266、218、231耐胆盐的能力较强；6株菌株均具有较好的耐渗透压的能力，其中菌株285对高渗透压的耐受性较强；菌株285和218在两种有机试剂中的疏水性均显著（P<0.05）高于其他菌株，且与十六烷的结合效果较好。发酵试验结果表明，6株菌株所发酵酸奶均在6~8 h内凝固，酸乳在冷藏期间，活菌数均保持在107 CFU/mL以上，均符合发酵剂的标准，其中菌株276的最高为3.22×106 CFU/mL；菌株218发酵制得的酸奶质构特性较好，持水力和酸化能力较其余菌株均最强，分别为60.98%和83 °T；菌株276、266抗后酸化能力较好；菌株231产香性能最优，乙醛含量为24~26 μg/mL，双乙酰含量为1.58~3.73 μg/mL，能够明显改善酸奶的风味。通过综合比较6株高产胞外多糖乳酸菌特性及发酵性能，菌株218为一株性能良好、具有良好稳定性的菌株，可作为乳酸菌发酵剂且具有一定的应用潜力。研究为利用四川藏区传统牦牛酸奶中分离出的高产胞外多糖乳酸菌在发酵乳制品的应用提供理论依据。     

High energy storage and ultrafast discharge in NaNbO3-based lead-free dielectric capacitors via a relaxor strategy

Dielectric capacitors with decent energy storage and fast charge-discharge performances are essential in advanced pulsed power systems. In this study, novel ceramics (1-x)NaNbO₃-xBi(Ni_2/3Nb_1/3)O₃(xBNN, x = 0.05, 0.1, 0.15 and 0.20) with high energy storage capability, large power density and ultrafast discharge speed were designed and prepared. The impedance analysis proves that the introducing an appropriate amount of Bi(Ni_0·5Nb_0.5)O₃ boosts the insulation ability, thus obtaining a high breakdown strength (E_b) of 440 kV/cm in xBNN ceramics. A high energy storage density (W_total) of 4.09 J/cm³, recoverable energy storage density (W_rec) of 3.31 J/cm³, and efficiency (η) of 80.9% were attained in the 0.15BNN ceramics. Furthermore, frequency and temperature stability (fluctuations of W_rec ≤ 0.4% over 5–100 Hz and W_rec ≤ 12.3% over 20–120 °C) were also observed. The 0.15BNN ceramics exhibited a large power density (19 MW/cm³) and ultrafast discharge time (~37 ns) over the range of ambient temperature to 120 °C. These enhanced performances may be attributed to the improved breakdown strength and relaxor behavior through the incorporation of BNN. In conclusion, these findings indicate that 0.15BNN ceramics may serve as promising materials for pulsed power systems.     

基于绿色建筑运营效果提升的室内环境评价方法

绿色建筑运营效果体现在两个方面,一个是基于其承担的环境效益的资源能源节约,另一个是基于其是为人所使用的人员满意效果,而人员满意效果则能够体现出室内环境的优劣.对室内环境的评价优先考虑人的使用满意程度,因此坚持以使用满意度为主要衡量指标,同时考虑人员满意度评估的随机性及不确定性因素,将室内客观数据作为补充.在评价过程中考虑绿色建筑运营评估的广泛推广及切实通过评价能够提升运营效果,选择最能够直接影响人员使用感受的指标内容,以促进后续运营效果提升的策略研究.     

Effect of cooking temperature on texture and flavour binding of braised sauce porcine skin

To investigate the effect of cooking temperature (55, 65, 75, 85 and 95 °C) on texture and flavour binding of braised sauce porcine skin (BSPS), sensory acceptance, microstructure and flavour-binding capacity were investigated during the processing of BSPS. Samples cooked at 85 and 95 °C showed better texture and aroma scores. Hardness and chewiness of BSPS were obviously improved at 85 and 95 °C than control group. Collagen structure was significantly destroyed over 85 °C. The porcine skin collagen heated at 85 and 95 °C showed relatively higher flavour-binding capacity than other samples. The improvement of texture of BSPS was mainly attributed to the degradation of collagen. Higher aroma scores of BSPS were related to intense binding abilities with aroma compounds at 85 and 95 °C. Cooking at 85 or 95 °C could be an optimal cooking temperature for BSPS.     

The effect of alkali metal oxide on the properties of borosilicate fireproof glass: Structure,thermal properties,viscosity, chemical stability

The purpose of the current work was to research the effect of alkali metal oxide on the structure, thermal properties, viscosity and chemical stability in the glass system (R₂O–CaO–B₂O₃–SiO₂) systematically. Because the glass would emulsify when Li₂O was added to the glass batch, this article did not discuss Li₂O. The results showed that when the amount of Na₂O was less than 4 mol.%, there was a higher interconnectivity of borate and silicate sub-networks in glass, as more mixed Si–O–B bonds were present in glass. The glass samples exhibited excellent thermal properties and chemical stabilities. As the amount of Na₂O exceeded 4 mol.%, the interconnectivity of borate and silicate sub-networks was weakened. The thermal properties and chemical stabilities of the glass samples were reduced. The connectivity of the silicate sub-network was weakened slightly as the Na/K ratio varied, and the coefficient of thermal expansion (CTE) of the glass samples gradually increased, and the resistance to thermal shock (RTS) value gradually decreased. Moreover, the viscosity of the glass samples decreased with the ratio of Na/Si and Na/K increased.     

Preparation and electrochemical characterization of Ti-based amorphous metallic glass with high strength

Ti-based amorphous metallic glasses have excellent mechanical, physical, and chemical properties, which is an important development direction and research hotspot of metal composite reinforcement. As a stable, simple, efficient, and large-scale preparation technology of metallic powders, the gas atomization process provides an effective way of preparing amorphous metallic glasses. In this study, the controllable fabrication of a Ti-based amorphous powder, with high efficiency, has been realized by using gas atomization. The scanning electron microscope, energy-dispersive spectrometer, and X-ray diffraction are used to analyze surface morphology, element distribution, and phase structure, respectively. A microhardness tester is used to measure the mechanical property. An electrochemical workstation is used to characterize corrosion behavior. The results show that as-prepared microparticles are more uniform and exhibit good amorphous characteristics. The mechanical test shows that the hardness of amorphous powder is significantly increased as compared with that before preparation, which has the prospect of being an important part of engineering reinforced materials. Further electrochemical measurement shows that the corrosion resistance of the as-prepared sample is also significantly improved. This study has laid a solid foundation for expanding applications of Ti-based metallic glasses, especially in heavy-duty and corrosive domains.     

Effects of (Li0.5Sm0.5)/W co-substitution and sintering temperature on the structure and electrical properties of ultrahigh Curie temperature piezoceramics,Ca0.92(Li0.5Sm0.5)0.08Bi2Nb2-xWxO9

With co-substitution of (Li_0.5Sm_0.5) at A site and W at B site, the electrical properties of modified Ca_0.92(Li_0.5Sm_0.5)_0.08Bi₂Nb_2-xW_xO₉ [(CLS)BN-xW, x = 0, 0.015 and 0.03] piezoceramics with ultrahigh Curie temperature (T_C) of > 930 °C were enhanced dramatically. The increased resistivity induced by the co-substitution ensure them to be polarized under an enough high field. Combined with the increase of spontaneous ferroelectric polarization (P_S), the significant enhancements in the piezoelectric, dielectric and ferroelectric properties can be obtained in the composition x = 0.015. Furthermore, the piezoelectric activity (d₃₃) and bulk resistivity (ρ_b) of (CLS)BN-0.015 W can be further enhanced at an appropriate sintering temperature. This optimum composition sintered at 1170 °C shows ultrahigh T_C of ～948 °C, d₃₃ of ～17.3 pC/N and ρ_b of ～6.9 MΩ cm at 600 °C, which are comparable to those of the reported high-temperature Aurivillius piezoceramics with T_C > 850 °C.